Morphological and elemental analysis of silver penetration into sound/demineralized dentin after SDF application.
Dent Mater. 2019 Sep 30;:
Authors: Sayed M, Matsui N, Uo M, Nikaido T, Oikawa M, Burrow MF, Tagami J
Abstract
OBJECTIVE: The aim of this study was to evaluate the penetration depth of silver into sound and demineralized dentin after application of silver diamine fluoride (SDF).
METHODS: Two hundred and eighty-eight dentin specimens were used. The specimens were divided into 3 groups: (1) sound dentin (control), (2) 30min EDTA-treated dentin; and (3) 13h EDTA-treated dentin. SDF was applied to all specimens. Each group was divided into 3 subgroups according to storage time into: 24h, 2 weeks and 1-year storage time. Each subgroup was further divided into four subgroups (n=8) according to different examinations as optical microscope (OM) observation, scanning electron microscopic (SEM) observation, elemental analysis with energy dispersive spectroscopy (EDS) and Micro-PIXE test.
RESULTS: The OM showed discoloration in the superficial layer after 24h and keep extending deeper after 2 weeks and 1-year. SEM showed silver crystals within dentinal tubules after 2 weeks and 1-year. EDS analysis can detect silver penetration only in the 1-year group reaching around 1200μm inside dentin. Micro-PIXE test detected silver at all time intervals, confirming the EDS depth results.
SIGNIFICANCE: It can be concluded that silver ions can completely infiltrate the demineralized dentin lesion with further penetration into the underlying mineralized dentin.