Resin Cement/Enamel Interface: A Morphological Evaluation of the Acid-Base Resistant Zone, Enamel Etching Pattern, and Effect of Thermocycling on the Microshear Bond Strength

J Adhes Dent. 2023 Mar 20;25:71-78. doi: 10.3290/j.jad.b3974603.

ABSTRACT

PURPOSE: To evaluate the effects of etching mode (self-etch and etch-and-rinse) on acid-base resistant zone (ABRZ) formation at the resin cement/enamel interface and enamel etching pattern, as well as the effects of thermocycling (0, 5000, and 10,000 cycles) on the enamel microshear bond strength (μSBS) mediated by dual-cure resin cements (DCRC).

MATERIALS AND METHODS: Two DCRC were used in 4 groups: Panavia V5 in self-etch (V5NE) and etch-and-rinse mode (V5E); and Estecem II in self-etch (ENE) and etch-and-rinse mode (EE). For ABRZ observation, the bonded interface was subjected to a demineralizing solution. The morphological attributes of the interface and etching patterns were observed using FE-SEM. For μ-SBS, cylinders with a 0.79-mm internal diameter and 0.5-mm height were made with DCRC and tested in shear after 0, 5000, and 10,000 thermal cycles (TC) (5°C and 55°C) (n = 10).

RESULTS: The formation of an enamel ABRZ was observed in all groups with different morphological features between self-etch and etch-and-rinse groups. A funnel-shaped erosion beneath the interface was present using V5NE and ENE modes where enamel was dissolved, while ABRZ formation was confirmed and no funnel-shaped erosion was noticed using V5E and EE. No significant differences in μSBS were observed between resin cements. However, significantly lower µSBSs were recorded when the self-etching mode was used. Thermocycling resulted in a significant reduction in µSBS for all groups.

CONCLUSION: Selective enamel etching should be recommended to improve the interfacial quality when dual-cure resin luting cements are used.

PMID:36939646 | DOI:10.3290/j.jad.b3974603