Cureus. 2023 Apr 25;15(4):e38090. doi: 10.7759/cureus.38090. eCollection 2023 Apr.

ABSTRACT

BACKGROUND: Biofilm deposit on the composite restoration is a common phenomenon and bacterial growth follows the deposition. The study aims to evaluate Streptococcus mutans (S. mutans) early biofilm formation on the surfaces of various dental composite resins by using the real-time quantitative polymerase chain reaction (qPCR) technique.

MATERIALS AND METHODS: Thirty-two discs, where eight discs were in each group of Filtek Supreme Ultra (FSU; 3M, St. Paul, MN), Clearfil AP-X (APX; Kuraray Noritake Dental Inc., Tokyo, Japan), Beautifil II (BE2; Shofu, Inc., Kyoto, Japan), and Estelite Sigma Quick (ESQ; Tokuyama Dental, Tokyo, Japan), were fabricated and subjected to S. mutans biofilm formation in an oral biofilm reactor for 12 hours. Contact angles (CA) were measured on the freshly fabricated specimen. The attached biofilms underwent fluorescent microscopy (FM). S. mutans from biofilms were analyzed using a qPCR technique. Surface roughness (Sa) measurements were taken before and after biofilm formation. Scanning electron microscopy (SEM), including energy dispersive X-ray spectrometer (EDS) analysis, was also performed for detecting relative elements on biofilms.

RESULTS: The study showed that FSU demonstrated the lowest CA while APX presented the highest values. FM revealed that condensed biofilm clusters were most on FSU. The qPCR results indicated the highest S. mutans DNA copies in the biofilm were on FSU while BE2 was the lowest (p < 0.05). Sa test signified that APX was significantly the lowest among all materials while FSU was the highest (p < 0.05). SEM displayed areas with apparently glucan-free S. mutans more on BE2 compared to APX and ESQ, while FSU had the least. Small white particles detected predominantly on the biofilms of BE2 appeared to be Si, Al, and F extruded from the resin.

CONCLUSION: Differences in early biofilm formation onto various composite resins are dependent on the differences in material compositions and their surface properties. BE2 showed the lowest quantity of biofilm accumulation compared to other resin composites (APX, ESQ, and FSU). This could be attributed to BE2 proprieties as a giomer and fluoride content.

PMID:37252523 | PMC:PMC10209747 | DOI:10.7759/cureus.38090

Cureus. 2023 Apr 25;15(4):e38090. doi: 10.7759/cureus.38090. eCollection 2023 Apr.

ABSTRACT

BACKGROUND: Biofilm deposit on the composite restoration is a common phenomenon and bacterial growth follows the deposition. The study aims to evaluate Streptococcus mutans (S. mutans) early biofilm formation on the surfaces of various dental composite resins by using the real-time quantitative polymerase chain reaction (qPCR) technique.

MATERIALS AND METHODS: Thirty-two discs, where eight discs were in each group of Filtek Supreme Ultra (FSU; 3M, St. Paul, MN), Clearfil AP-X (APX; Kuraray Noritake Dental Inc., Tokyo, Japan), Beautifil II (BE2; Shofu, Inc., Kyoto, Japan), and Estelite Sigma Quick (ESQ; Tokuyama Dental, Tokyo, Japan), were fabricated and subjected to S. mutans biofilm formation in an oral biofilm reactor for 12 hours. Contact angles (CA) were measured on the freshly fabricated specimen. The attached biofilms underwent fluorescent microscopy (FM). S. mutans from biofilms were analyzed using a qPCR technique. Surface roughness (Sa) measurements were taken before and after biofilm formation. Scanning electron microscopy (SEM), including energy dispersive X-ray spectrometer (EDS) analysis, was also performed for detecting relative elements on biofilms.

RESULTS: The study showed that FSU demonstrated the lowest CA while APX presented the highest values. FM revealed that condensed biofilm clusters were most on FSU. The qPCR results indicated the highest S. mutans DNA copies in the biofilm were on FSU while BE2 was the lowest (p < 0.05). Sa test signified that APX was significantly the lowest among all materials while FSU was the highest (p < 0.05). SEM displayed areas with apparently glucan-free S. mutans more on BE2 compared to APX and ESQ, while FSU had the least. Small white particles detected predominantly on the biofilms of BE2 appeared to be Si, Al, and F extruded from the resin.

CONCLUSION: Differences in early biofilm formation onto various composite resins are dependent on the differences in material compositions and their surface properties. BE2 showed the lowest quantity of biofilm accumulation compared to other resin composites (APX, ESQ, and FSU). This could be attributed to BE2 proprieties as a giomer and fluoride content.

PMID:37252523 | PMC:PMC10209747 | DOI:10.7759/cureus.38090

Cureus. 2023 Apr 25;15(4):e38090. doi: 10.7759/cureus.38090. eCollection 2023 Apr.

ABSTRACT

BACKGROUND: Biofilm deposit on the composite restoration is a common phenomenon and bacterial growth follows the deposition. The study aims to evaluate Streptococcus mutans (S. mutans) early biofilm formation on the surfaces of various dental composite resins by using the real-time quantitative polymerase chain reaction (qPCR) technique.

MATERIALS AND METHODS: Thirty-two discs, where eight discs were in each group of Filtek Supreme Ultra (FSU; 3M, St. Paul, MN), Clearfil AP-X (APX; Kuraray Noritake Dental Inc., Tokyo, Japan), Beautifil II (BE2; Shofu, Inc., Kyoto, Japan), and Estelite Sigma Quick (ESQ; Tokuyama Dental, Tokyo, Japan), were fabricated and subjected to S. mutans biofilm formation in an oral biofilm reactor for 12 hours. Contact angles (CA) were measured on the freshly fabricated specimen. The attached biofilms underwent fluorescent microscopy (FM). S. mutans from biofilms were analyzed using a qPCR technique. Surface roughness (Sa) measurements were taken before and after biofilm formation. Scanning electron microscopy (SEM), including energy dispersive X-ray spectrometer (EDS) analysis, was also performed for detecting relative elements on biofilms.

RESULTS: The study showed that FSU demonstrated the lowest CA while APX presented the highest values. FM revealed that condensed biofilm clusters were most on FSU. The qPCR results indicated the highest S. mutans DNA copies in the biofilm were on FSU while BE2 was the lowest (p < 0.05). Sa test signified that APX was significantly the lowest among all materials while FSU was the highest (p < 0.05). SEM displayed areas with apparently glucan-free S. mutans more on BE2 compared to APX and ESQ, while FSU had the least. Small white particles detected predominantly on the biofilms of BE2 appeared to be Si, Al, and F extruded from the resin.

CONCLUSION: Differences in early biofilm formation onto various composite resins are dependent on the differences in material compositions and their surface properties. BE2 showed the lowest quantity of biofilm accumulation compared to other resin composites (APX, ESQ, and FSU). This could be attributed to BE2 proprieties as a giomer and fluoride content.

PMID:37252523 | PMC:PMC10209747 | DOI:10.7759/cureus.38090

Cureus. 2023 Apr 25;15(4):e38090. doi: 10.7759/cureus.38090. eCollection 2023 Apr.

ABSTRACT

BACKGROUND: Biofilm deposit on the composite restoration is a common phenomenon and bacterial growth follows the deposition. The study aims to evaluate Streptococcus mutans (S. mutans) early biofilm formation on the surfaces of various dental composite resins by using the real-time quantitative polymerase chain reaction (qPCR) technique.

MATERIALS AND METHODS: Thirty-two discs, where eight discs were in each group of Filtek Supreme Ultra (FSU; 3M, St. Paul, MN), Clearfil AP-X (APX; Kuraray Noritake Dental Inc., Tokyo, Japan), Beautifil II (BE2; Shofu, Inc., Kyoto, Japan), and Estelite Sigma Quick (ESQ; Tokuyama Dental, Tokyo, Japan), were fabricated and subjected to S. mutans biofilm formation in an oral biofilm reactor for 12 hours. Contact angles (CA) were measured on the freshly fabricated specimen. The attached biofilms underwent fluorescent microscopy (FM). S. mutans from biofilms were analyzed using a qPCR technique. Surface roughness (Sa) measurements were taken before and after biofilm formation. Scanning electron microscopy (SEM), including energy dispersive X-ray spectrometer (EDS) analysis, was also performed for detecting relative elements on biofilms.

RESULTS: The study showed that FSU demonstrated the lowest CA while APX presented the highest values. FM revealed that condensed biofilm clusters were most on FSU. The qPCR results indicated the highest S. mutans DNA copies in the biofilm were on FSU while BE2 was the lowest (p < 0.05). Sa test signified that APX was significantly the lowest among all materials while FSU was the highest (p < 0.05). SEM displayed areas with apparently glucan-free S. mutans more on BE2 compared to APX and ESQ, while FSU had the least. Small white particles detected predominantly on the biofilms of BE2 appeared to be Si, Al, and F extruded from the resin.

CONCLUSION: Differences in early biofilm formation onto various composite resins are dependent on the differences in material compositions and their surface properties. BE2 showed the lowest quantity of biofilm accumulation compared to other resin composites (APX, ESQ, and FSU). This could be attributed to BE2 proprieties as a giomer and fluoride content.

PMID:37252523 | PMC:PMC10209747 | DOI:10.7759/cureus.38090

Cureus. 2023 Apr 25;15(4):e38090. doi: 10.7759/cureus.38090. eCollection 2023 Apr.

ABSTRACT

BACKGROUND: Biofilm deposit on the composite restoration is a common phenomenon and bacterial growth follows the deposition. The study aims to evaluate Streptococcus mutans (S. mutans) early biofilm formation on the surfaces of various dental composite resins by using the real-time quantitative polymerase chain reaction (qPCR) technique.

MATERIALS AND METHODS: Thirty-two discs, where eight discs were in each group of Filtek Supreme Ultra (FSU; 3M, St. Paul, MN), Clearfil AP-X (APX; Kuraray Noritake Dental Inc., Tokyo, Japan), Beautifil II (BE2; Shofu, Inc., Kyoto, Japan), and Estelite Sigma Quick (ESQ; Tokuyama Dental, Tokyo, Japan), were fabricated and subjected to S. mutans biofilm formation in an oral biofilm reactor for 12 hours. Contact angles (CA) were measured on the freshly fabricated specimen. The attached biofilms underwent fluorescent microscopy (FM). S. mutans from biofilms were analyzed using a qPCR technique. Surface roughness (Sa) measurements were taken before and after biofilm formation. Scanning electron microscopy (SEM), including energy dispersive X-ray spectrometer (EDS) analysis, was also performed for detecting relative elements on biofilms.

RESULTS: The study showed that FSU demonstrated the lowest CA while APX presented the highest values. FM revealed that condensed biofilm clusters were most on FSU. The qPCR results indicated the highest S. mutans DNA copies in the biofilm were on FSU while BE2 was the lowest (p < 0.05). Sa test signified that APX was significantly the lowest among all materials while FSU was the highest (p < 0.05). SEM displayed areas with apparently glucan-free S. mutans more on BE2 compared to APX and ESQ, while FSU had the least. Small white particles detected predominantly on the biofilms of BE2 appeared to be Si, Al, and F extruded from the resin.

CONCLUSION: Differences in early biofilm formation onto various composite resins are dependent on the differences in material compositions and their surface properties. BE2 showed the lowest quantity of biofilm accumulation compared to other resin composites (APX, ESQ, and FSU). This could be attributed to BE2 proprieties as a giomer and fluoride content.

PMID:37252523 | PMC:PMC10209747 | DOI:10.7759/cureus.38090

J Adhes Dent. 2023 Mar 20;25(1):71-78. doi: 10.3290/j.jad.b3974603.

ABSTRACT

PURPOSE: To evaluate the effects of etching mode (self-etch and etch-and-rinse) on acid-base resistant zone (ABRZ) formation at the resin cement/enamel interface and enamel etching pattern, as well as the effects of thermocycling (0, 5000, and 10,000 cycles) on the enamel microshear bond strength (μSBS) mediated by dual-cure resin cements (DCRC).

MATERIALS AND METHODS: Two DCRC were used in 4 groups: Panavia V5 in self-etch (V5NE) and etch-and-rinse mode (V5E); and Estecem II in self-etch (ENE) and etch-and-rinse mode (EE). For ABRZ observation, the bonded interface was subjected to a demineralizing solution. The morphological attributes of the interface and etching patterns were observed using FE-SEM. For μ-SBS, cylinders with a 0.79-mm internal diameter and 0.5-mm height were made with DCRC and tested in shear after 0, 5000, and 10,000 thermal cycles (TC) (5°C and 55°C) (n = 10).

RESULTS: The formation of an enamel ABRZ was observed in all groups with different morphological features between self-etch and etch-and-rinse groups. A funnel-shaped erosion beneath the interface was present using V5NE and ENE modes where enamel was dissolved, while ABRZ formation was confirmed and no funnel-shaped erosion was noticed using V5E and EE. No significant differences in μSBS were observed between resin cements. However, significantly lower µSBSs were recorded when the self-etching mode was used. Thermocycling resulted in a significant reduction in µSBS for all groups.

CONCLUSION: Selective enamel etching should be recommended to improve the interfacial quality when dual-cure resin luting cements are used.

PMID:36939646 | DOI:10.3290/j.jad.b3974603

J Adhes Dent. 2023 Mar 20;25(1):71-78. doi: 10.3290/j.jad.b3974603.

ABSTRACT

PURPOSE: To evaluate the effects of etching mode (self-etch and etch-and-rinse) on acid-base resistant zone (ABRZ) formation at the resin cement/enamel interface and enamel etching pattern, as well as the effects of thermocycling (0, 5000, and 10,000 cycles) on the enamel microshear bond strength (μSBS) mediated by dual-cure resin cements (DCRC).

MATERIALS AND METHODS: Two DCRC were used in 4 groups: Panavia V5 in self-etch (V5NE) and etch-and-rinse mode (V5E); and Estecem II in self-etch (ENE) and etch-and-rinse mode (EE). For ABRZ observation, the bonded interface was subjected to a demineralizing solution. The morphological attributes of the interface and etching patterns were observed using FE-SEM. For μ-SBS, cylinders with a 0.79-mm internal diameter and 0.5-mm height were made with DCRC and tested in shear after 0, 5000, and 10,000 thermal cycles (TC) (5°C and 55°C) (n = 10).

RESULTS: The formation of an enamel ABRZ was observed in all groups with different morphological features between self-etch and etch-and-rinse groups. A funnel-shaped erosion beneath the interface was present using V5NE and ENE modes where enamel was dissolved, while ABRZ formation was confirmed and no funnel-shaped erosion was noticed using V5E and EE. No significant differences in μSBS were observed between resin cements. However, significantly lower µSBSs were recorded when the self-etching mode was used. Thermocycling resulted in a significant reduction in µSBS for all groups.

CONCLUSION: Selective enamel etching should be recommended to improve the interfacial quality when dual-cure resin luting cements are used.

PMID:36939646 | DOI:10.3290/j.jad.b3974603