Effect of solvent evaporation strategies on regional bond strength of one-step self-etch adhesives to root canal dentine.
Int Endod J. 2013 Feb 23;
Authors: Thitthaweerat S, Nakajima M, Foxton RM, Tagami J
Abstract
AIM: To evaluate the efficacy of different solvent evaporation strategies on bonding of one-step self-etch adhesives to root canal dentine. METHODOLOGY: Two dual-cure resin core systems (Clearfil DC Bond/Clearfil DC Core Automix and Clearfil Tri-S Bond Plus/Clearfil DC Core Plus; Kuraray Noritake Dental, Tokyo, Japan) were equally applied in 24 post spaces from extracted human mandibular premolars. After the adhesive application, specimens were randomly assigned into four water/solvent evaporation strategies as follows (I) insertion of absorbent paper point for 10 s: P, (II) 10 s air-blowing: A, (III) as (II) followed by insertion of absorbent paper point: AP, (IV) as (III) followed by 10 s additional air-blowing: APA. Then, the adhesives were light cured, and resin core materials were placed into the post space, followed by light curing for 60 s. After water storage for 24 h, 0.6 × 0.6 mm-thick beams were prepared to measure the regional μTBS. The mode of failure was also observed. The μTBS values were statistically analysed using three-way anova and Duncan HSD test (α = 0.05). RESULTS: In the coronal region, there were no significant differences in μTBS between each evaporation strategy (P > 0.05), except P group. However, in the apical region, APA and AP groups significantly increased in μTBS compared with A and P groups (P < 0.05). Only in the APA group of Clearfil Tri-S Bond Plus/Clearfil DC Core Plus, was there no significant difference in μTBS between the coronal and apical regions (P > 0.05). CONCLUSION: The use of paper points with additional air-blowing for removing excessive adhesive and evaporating residual water/solvent would be effective in producing higher bond strength for the tested one-step self-etch adhesives and fewer blister formations in deeper regions of the post space.
[cite source='pubmed']23521044[/cite] – as supplied by publisher]